BASE OR BODY: It is advisable to use red biscuit, terracotta or white body for the best development of the metal effect.

These glazes are suitable only for decoration purpose, not for ceramicware.

GLAZED OF THE PIECES: by aerograph for the greatest homogeneity of the coat, but always bearing in mind that:

-An excess of coat causes the dripping of the glaze because this kind of glazes are very flux.
-A little coat causes transparencies and there is not development of the metal effect.

FIRING TEMPERATURE: 980 - 1040ºC.

Peso
12,90 €
Tasse incluse
Quantità

Descrizione
Technical data printed from i-Fites Prodesco (c) 2003 Ideas Sistemas Informáticos S.L. - Nazaret 2, bajo - 46520 Pto. Sagunto - Valencia – Spain – Phone# +34 96 269 8169 – Fax# +34 96 269 8170
Page 1 of 1
CREATION: 15/09/2021 REVISION:15/09/2021 (Rev. 2)
TECHNICAL DATA 'ESMALTE 5841 LUSTRADO SERIG. POLVO Printed: 15/09/2021
1. IDENTIFICATION OF THE SUBSTANCE
Code 22246004
Product name 'ESMALTE 5841 LUSTRADO SERIG. POLVO
Description LUSTERED GLAZE BLACK.
It belongs to the LISTERED glazes. These glazes are not for ceramicware
Compound of frit: CAS Nº. 65997-18-4.
Application It is advisable to use red biscuit, terracotta or white body or over an engobe.
The glazed of the pieces is recommended by aerograph for the greatest homogeneity of the coat (an excess of
coat causes the dripping of the glaze and a little not develop of the metal effect)
In general, they can be used as much for quick cycle as for muffle. The temperature range is from 980 to 1040
° C. Temperature maintenance: 30 or 40 minutes
according to the application and the firing temperature, different results are obtained.
For additional information you can visit our page https://prodesco.es/ing/almacen.asp?n1=7&n2=36
Company
PRODESCO S.L.. Phone# 961545588
C/ Aviación 44 Fax# 961533025
46940 Manises e-mail admon@prodesco.es
Valencia - España Web http://www.prodesco.es
2. INFORMATION AND COMPOSITION ON SUBSTANCES
Chemical analyses
Li2O ZnO Cr2O3 CaF2
Na2O [0-0,5] MnO B2O3 Bi2O3
K2O [0-0,5] CdO V2O5 [1-5] P2O5
MgO CoO MnO2 BeO
CaO [0-0,5] NiO SiO2 [20-40] CeO2
SrO Al2O3 [1-5] TiO2 [1-5] CuO
BaO Fe2O3 [5-10] ZrO2 Pr2O3
PbO [40-80] Sb2O3 SnO2
3 PHYSICAL AND CHEMICAL PROPERTIES
Aspect Grey powder Acid index 1,34
State Solid Superficial tension 225,73din/cm
Colour(fired) Black Bright Lustered
Odour
4. COLOUR PARAMETERS
* From Minolta ChromaControl (S)
5. COEFFICIENT OF THERMAL EXPANSION
(25-300) 79 1710 −− C Transformation temperature 496ºC
(50-300) 79 1710 −− C Softening temperature 591ºC
(300-500) 99 1710 −− C Fusion point >980ºC
(500-600) 1710 −− C
* Dates Obtained from dilatometer BÄHR mod. DIL 801 L.
6. PARTICLE SIZE DISTRIBUTION
7. RECOMMENDATIONS ON GLAZED OBJECTS DESTINED TO CULINARY USE
5.NOT RECOMMEND
It is not recommended to culinary use only decoration use.
*L= 44.85 *A= 0.37 *B= -4.08
Size: >10μ 59,92% Refraction: 1,68
>25μ 29,08% Absorbing: 0,05
>50μ 13,47%
>70μ 2,24%
>100μ 0%
d(0,5) 13,824
μ * Dates Obtained from Malvern Instr
Dettagli del prodotto
5841

Recensioni

Ancora nessuna recensione da parte degli utenti.

Scrivi la tua recensione

CLA3 cristallina lucida apiombica neutra per immersione

5841 Smalto Nero speciale

BASE OR BODY: It is advisable to use red biscuit, terracotta or white body for the best development of the metal effect.

These glazes are suitable only for decoration purpose, not for ceramicware.

GLAZED OF THE PIECES: by aerograph for the greatest homogeneity of the coat, but always bearing in mind that:

-An excess of coat causes the dripping of the glaze because this kind of glazes are very flux.
-A little coat causes transparencies and there is not development of the metal effect.

FIRING TEMPERATURE: 980 - 1040ºC.